Beech granulate 0.75–3.0 mm – control (no fibres) · G. lucidum (BM)
✓ Reviewed content
Ganoderma lucidum (M9726) · Centre for IT and Architecture (CITA), Royal Danish Academy, Copenhagen (DK)
Recipe
How this sample was made, step by step · total growth 28 days-
1
Substrate
- Beech wood granulate HB 750/2000 (0.75–3 mm; J. Rettenmaier & Söhne GmbH + Co KG, Rosenberg (DE))
-
2
Sterilisation
- Method
- Autoclaving
- Details
- 121 °C, 15 min (substrate, fibres and fabric)
-
3
Inoculation
- Fungus
- Ganoderma lucidum · M9726
- Inoculum
- Grain spawn
- Rate
- 16 wt%
- Water content
- 40 %
-
4
Pre-growth
7 days- Where
- bag / container
-
5
Growth in mould
21 days- Mould
- aerated PETG moulds; pre-growth in PP filter bags (SacO2 PPD50/REH4+1/V22-49)
- Temperature
- 25 °C
- Light
- dark
-
6
Inactivation
- Method
- Oven drying
- Temperature
- 60 °C
- Duration
- 48 h
-
7
Specimen & testing
- Geometry
- prism 36 × 36 × 144 mm (nominal), dried 34 × 34 × 140 mm
- Dry density
- 233.87 kg/m³
- Measurements
- 3
Pre-growth 7 daysGrowth in mould 21 days
Steps marked “not reported” were not stated in the source. Suggest missing details
Beech wood granulate 0.75–3.0 mm, control (no fibres). Grown without an external mycelium skin.
Measurements
Mechanical
| Property | Value | n | Test standard | Conditions | |
|---|---|---|---|---|---|
| Compressive strength | 0.30638 ± 0.05764 MPa | 6 | ASTM D1037 (compression parallel to surface, short-column method) | stored at 4 °C / 65 % RH before testing ultimate strength, 306.38 ± 57.64 kPa in the paper; 1.0 mm/min |
edit |
| Compressive modulus | 3.32 ± 0.8 MPa | 6 | ASTM D1037 (compression parallel to surface, short-column method) | stored at 4 °C / 65 % RH before testing 1.0 mm/min |
edit |
Physical properties
Production
Substrate mix
Fungus & inoculation
- Fungus
- Ganoderma lucidum (M9726)
- Inoculum type
- Grain spawn
- Inoculation rate [wt%]
- 16
- Water content at inoculation [%]
- 40
- Sterilisation
- Autoclaving
- Sterilisation – details
- 121 °C, 15 min (substrate, fibres and fabric)
Growth
- Pre-growth (bag) [days]
- 7
- Growth in mould [days]
- 21
- Temperature [°C]
- 25
- Light
- dark
- Mould / mould material
- aerated PETG moulds; pre-growth in PP filter bags (SacO2 PPD50/REH4+1/V22-49)
Post-processing
- Inactivation
- Oven drying
- Inactivation – temperature [°C]
- 60
- Inactivation – duration [h]
- 48
Specimen
- Specimen geometry
- prism 36 × 36 × 144 mm (nominal), dried 34 × 34 × 140 mm
- Dry density [kg/m³]
- 233.87
Notes
Substrate, fibres and fabric adjusted to 40 % moisture with mineral water; mixed with 16 wt% spawn, 7 days in the bag, then broken up and packed into the mould together with the fibres.
Community feedback
Is something wrong or confirmed by your own tests? Mark the experiment as ✓ correct or ✗ not correct and explain why.