EFB + Albizia sawdust, hot-pressed, wood-oil coated · G. lucidum (DMC)
✓ Reviewed content
Ganoderma lucidum (M 9720) · National University of Singapore (SG); Karlsruhe Institute of Technology (DE)
Recipe
How this sample was made, step by step · total growth 14 days-
1
Substrate
- Oil palm empty fruit bunch fibres (EFB) (Heng Huat Group (MY))
- Albizia sawdust (≤ 2 mm; San Ho Timber Workshop, Singapore)
- Wheat bran (Bob’s Red Mill (US))
- Calcium carbonate (CaCO₃) (LushGro (SG))
- Pre-treatment
- pre-dried at 70 °C for 2 h (approx. 10 % moisture), water:EFB 5:4 by mass; pre-dried at 70 °C for 2 h, particles > 2 mm sieved out (Fritsch sieve shaker)
-
2
Sterilisation
- Method
- Autoclaving
- Details
- 120 °C, 60 min (sawdust, spawn); at least 20 min (EFB)
-
3
Inoculation
- Fungus
- Ganoderma lucidum · M 9720
- Inoculum
- Grain spawn
- Rate
- 0.1 wt%
- Water content
- 60 %
-
4
Pre-growth
14 days- Where
- bag / container
- Temperature
- 27 °C
- Humidity
- 75 % RH
-
5
Growth in mould
- Mould
- block moulds type A (23.1 L) and type B (16.5 L)
-
6
Inactivation & pressing
- Method
- Oven drying
- Temperature
- 70 °C
- Duration
- 48 h
- Pressure
- 20 MPa
-
7
Finishing
- Coating
- oil-based coating, Osmo Holz und Color (Warendorf), per manufacturer’s instructions
-
8
Specimen & testing
- Geometry
- specimens CNC-cut from the pressed board (dimensions in Fig. 1 of the paper)
- Dry density
- 954 kg/m³
- Measurements
- 8
Steps marked “not reported” were not stated in the source. Suggest missing details
Dense mycelium board with oil-based coating (Osmo).
Measurements
Mechanical
| Property | Value | n | Test standard | Conditions | |
|---|---|---|---|---|---|
| Compressive strength | 3.36 ± 1.12 MPa | 3 | ASTM D1037 (modified) | unweathered (day 0) 0.5 mm/min |
edit |
| Compressive strength | 2.21 ± 0.98 MPa | 3 | ASTM D1037 (modified) | 35 days climate chamber 27.5 ± 2.5 °C / 75 ± 15 % RH, no UV 0.5 mm/min |
edit |
| Tensile strength | 1.53 ± 0.27 MPa | 3 | ASTM D1037 (modified) | unweathered (day 0) 3 mm/min |
edit |
| Tensile strength | 0.81 ± 0.02 MPa | 3 | ASTM D1037 (modified) | 35 days climate chamber 27.5 ± 2.5 °C / 75 ± 15 % RH, no UV 3 mm/min |
edit |
| Tensile modulus | 602.2 ± 87.9 MPa | 3 | ASTM D1037 (modified) | unweathered (day 0) 3 mm/min, Epsilon 3542 extensometer |
edit |
| Tensile modulus | 286.1 ± 81.7 MPa | 3 | ASTM D1037 (modified) | 35 days climate chamber 27.5 ± 2.5 °C / 75 ± 15 % RH, no UV 3 mm/min, Epsilon 3542 extensometer |
edit |
| Flexural strength | 2.53 ± 0.81 MPa | 3 | ASTM D1037 (modified), 4-point bending | unweathered (day 0) support span 210 mm, loading span 70 mm, 2 mm/min |
edit |
| Flexural strength | 1.62 ± 0.28 MPa | 3 | ASTM D1037 (modified), 4-point bending | 35 days climate chamber 27.5 ± 2.5 °C / 75 ± 15 % RH, no UV support span 210 mm, loading span 70 mm, 2 mm/min |
edit |
Production
Substrate mix
Fungus & inoculation
- Fungus
- Ganoderma lucidum (M 9720)
- Inoculum type
- Grain spawn
- Inoculation rate [wt%]
- 0.1
- Water content at inoculation [%]
- 60
- Sterilisation
- Autoclaving
- Sterilisation – details
- 120 °C, 60 min (sawdust, spawn); at least 20 min (EFB)
Growth
- Pre-growth (bag) [days]
- 14
- Temperature [°C]
- 27
- Relative humidity [%]
- 75
- Mould / mould material
- block moulds type A (23.1 L) and type B (16.5 L)
Post-processing
- Inactivation
- Oven drying
- Inactivation – temperature [°C]
- 70
- Inactivation – duration [h]
- 48
- Pressing pressure [MPa]
- 20
- Coating / surface treatment
- oil-based coating, Osmo Holz und Color (Warendorf), per manufacturer’s instructions
Specimen
- Specimen geometry
- specimens CNC-cut from the pressed board (dimensions in Fig. 1 of the paper)
- Dry density [kg/m³]
- 954
Notes
Spawn: wheat grains/wheat bran/CaCO₃ 88/10/2 wt% + 20 wt% water, 2 weeks at 26–28 °C and 70–80 % RH. Sawdust mix 88/10/2 wt% (sawdust/bran/CaCO₃) + 60 wt% water, 1 kg bags with 1 g spawn, colonised for 2 weeks. Then mixed with sterilised EFB fibres in a volume ratio EFB:sawdust 4:3 and filled into block moulds (wet density approx. 239 kg/m³); 4–5 days in the mould, 3–4 days without (7–9 days in total). Dried for 2 days at 70 °C (block density 120–130 kg/m³), then hot-pressed for 50 min at 120 °C and 20 MPa and post-cured for 24 h at 50 °C (board density approx. 954 kg/m³). Temperature and humidity entered as the middle of the range.